INTERNATIONAL JOURNAL OF PROSTHODONTICS, cilt.34, sa.5, ss.608-614, 2021 (SCI-Expanded)
Purpose: To analyze the load to failure of different CAD/CAM high-density polymers (HDPs) and zirconia when titanium (Ti) bases were included in a cantilevered situation. Materials and Methods: Five specimens were fabricated from five different CAD/CAM polymethyl methacrylate (PMMA) HDPs (Copratemp [CT]; Tempo-CAD [TC]; Solid Shade PMMA Disc [TD]; M-PM Disc pink [MPM]; M-PM Disc white [MPMW]), and five specimens were prepared from an yttrium-stabilized tetragonal zirconia (3Y-TZP; FireZr [FZR]; control). Ti bases (D Master Dental Implants) were cemented onto the specimens (8 mm thick x 7 mm wide x 30 mm long). Each specimen was fixated using a clamp for a cantilever loading distance of 10 mm. The load was applied on the cantilever until failure, and the maximum load to failure values (N) were analyzed using analysis of variance (GLIMMIX procedure) with a log-normal error distribution in addition to the restricted maximum likelihood estimation method to eliminate the need for equality of variances and Tukey Honest Significant Difference test (alpha = .05). Results: Differences among the load-to-failure values of HDPs were not significant (P > .05); however, zirconia had significantly higher load-to-failure values than HDPs (P < .001). The behavior of HDPs and zirconia under loading was different in terms of displacement. HDPs showed weaker but more ductile behavior than zirconia, which is stronger, but more brittle. Conclusion: The tested brands of HDPs performed similarly under loading. Zirconia with a Ti base showed higher strength compared to all tested HDPs with a Ti base. The loads that fractured the specimens with Ti bases were close to the maximum occlusal bite forces recorded in previous clinical studies.