Comparison of Levitation Forces of Bulk MgB2 Superconductors Produced by Nano Boron and Carbon-Doped Nano Boron

Duz I., Guner S. B., Erdem O., Demir I., Kapucu V., Celik S., ...Daha Fazla

JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, cilt.27, sa.10, ss.2241-2247, 2014 (SCI-Expanded, Scopus) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 27 Sayı: 10
  • Basım Tarihi: 2014
  • Doi Numarası: 10.1007/s10948-014-2602-4
  • Dergi Adı: JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.2241-2247
  • Anahtar Kelimeler: MgB2 superconductors, Levitation force, Hot press
  • Ankara Üniversitesi Adresli: Evet

Özet

MgB2 bulk superconductors were prepared by hot press plus furnace heating method. Two types of boron powders were used, one is amorphous nano boron and the other is C-doped boron. Characteristics of superconductors were determined by XRD and resistance measurements. Systematic levitation force measurements were performed by using a modular system at low temperatures. These bulk superconductors showed around 9 N repulsive and 4 N attractive forces in the z-axis at 20 K at closest point to the cryostat lid which contains the MgB2 superconductor. These values slightly decreased by increasing temperature to 24 and 28 K for both samples. Comparing two samples, nano boron MgB2 showed slightly higher levitation force than C-doped MgB2 although C-doped MgB2 has higher attractive force value at the closest point. This situation points out that C-doped MgB2 is much proper for attractive force applications (as guidance force) while the nanoboron MgB2 sample is much appropriate for repulsive force (as levitation).